PP Raffia Granules
H030SG Reliance PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Types Of PP Granules | Natural |
Form | Granules |
Brand | Reliance |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | H030SG |
Country of Origin | Made in India |
Melt Flow Rate (230 deg C/2.16 kg) | 3.4 g/10 min |
Tensile Strength at Yield (50 mm/min) | 34 MPa |
Elongation at Yield (50 mm/min) | 10% |
Flexural Modulus (1% secant) | 1650 MPa |
Notched Izod Impact Strength (23 deg C) | 40 J/m |
Heat Deflection Temperature (455 kPa) | 10 deg C |
Applications:
- Woven fabrics, sacks & monofilaments
Regulatory Information:
- Meets the requirements stipulated in IS 10910 on 'Specification for Polypropylene and its Copolymers for safe use in contact with foodstuff, pharmaceuticals, and drinking water'. Additives incorporated in this grade conform to the positive list of constituents as prescribed in IS 10909. The grade and the additives incorporated in it also comply with the FDA:CFR Title 21,177.1520, Olefin polymers
Storage Recommendations:
- Bags should be stored in dry/ closed conditions at temperatures below 50°C and protected from UV/direct sunlight
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5
RH03 OPAL PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Types Of PP Granules | Natural |
Form | Granules |
Brand | OPAL |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | RH03 |
Country of Origin | Made in India |
Melt Flow Index ( 230 deg C & 2.16 kg) | 3.3 g/10 min |
Density (23 deg C) | 3 0.90 Gm/cm |
Tensile Strength @ Yield (50mm / min) | 35 MPa |
Elongation @ Yield (50mm / min) | 10 % |
Flexural Modulus (1.3 mm/min) | 1500 MPa |
Notch Izod Impact Strength ( @ 23 deg C) | 50 J/m |
Hardness (Rockwell) | 100 R Scale |
Vicat Softening Point (10N) | 150 deg C |
Heat Deflection Temperature (0.46N/m2) | 95 deg C |
PP Homo Polymer RH03 is a natural colored high performance grade produced with the latest Ineos Gas Phase polymerization Technology exhibiting following features:
- Very good processability.
- Good balance of tenacity & elongation.
- Low water carry-over.
PP Homo Polymer RH03 is recommended for following oriented structures (Stretched Tapes) applications:
- Cement Packaging bags
- Fertilizer Packaging bags
- Food Grain Packaging bags
- Bulk Industrial Packaging (FIBC)
- General purpose wrapping fabric
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT
HP30G Aramco PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Form | Granules |
Types Of PP Granules | Natural |
Brand | Aramco |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | HP30G |
Flexural Strength | 35 MPa |
Country of Origin | Made in India |
Tensile Strength at Yield | 34 MPa |
Tensile Elongation at Yield | 9 % |
Tensile Strength at Break | 19 MPa |
Tensile Elongation at Break | 165 % |
Flexural Modulus | 1300 MPa |
Izod Impact, Notched 23 deg C | 3.0 kJ/m2 |
Hardness Rockwell | 98 |
Aramco PP HP30G is a homopolymer polypropylene resin and is typically used for yarn extrusion characterized by ease of processing and low heat shrinkage. Yarn made from this resin typically exhibits excellent mechanical properties. This product is also typically used for thermoforming application.
Typical Applications:
- Woven sacks, woven cloths, monofilament, binding tape, thermoforming. This product is not intended for use in medical and pharmaceutical applications.
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT
H1030 Tasnee PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Density | 0.9 g/cm3 |
Types Of PP Granules | Natural |
Form | Granules |
Brand | Tasnee |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | H1030 |
Melt Flow Rate (230 deg C/2.16 kg) | 3 g/10min |
Melting Temperature | 163 deg C |
Vicat Softening Temperature | 152 deg C |
Heat Distortion Temperature @ 0.45 MPa | 102 deg C |
Tensile Strength @ Yield | 33 MPa |
Tensile Elongation @ Yield | 10 % |
Flexural Modulus (1% Secant) | 1450 MPa |
Charpy Impact Strength (Notched) at 23 deg C | 4.0 KJ/m2 |
Rockwell Hardness | 100 R |
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT
Marlex HGX030SP Polypropylene Homopolymer Raffia Grade
Minimum Order Quantity: 500 Kg
Product Brochure
Plastic Type | granules |
Color | Natural |
Usage/Application | General Plastics |
Material | Poly Propylene |
Density | 0.906 g/cm3 |
Types Of PP Granules | Natural |
Brand | Marlex |
Packaging Type | Bag |
Packaging Size | 25kgs |
Grade | HGX030SP |
Melt Flow Rate | 3 g/10 min |
I Deal In | New Only |
Recycled | No |
Mechanical properties were determined using injection-moulded specimens 3.2 mm thick, moulded per ASTM D4101, unless otherwise noted.
Additional Information:
- Delivery Time: 2-3 Days
- Packaging Details: 25kgs bag (Goni)
Advanced PP 1102K Polypropylene Homopolymer Raffia Grade
Minimum Order Quantity: 500 Kg
Plastic Type | granules |
Color | Natural |
Usage/Application | General Plastics |
Material | Poly Propylene |
Density | 0.91 |
Types Of PP Granules | Natural |
Brand | Advanced |
Packaging Type | Bag |
Packaging Size | 25kgs |
Melting Point | 163 DegreeC |
Grade | 1102K |
Heat Distortion Temperature | 85 DegreeC |
Melt Flow Rate | 3.4 g / 10 min |
Model Name/Number | 1102K |
I Deal In | New Only |
Recycled | No |
Applications Raffia, Thermoformed parts, Tape yarns, monofilament, strapping
Regulatory Information:
The Grade Advanced-PP 1102K and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011 (and its amendments). Specific information is available upon request
Additional Information:
- Delivery Time: 2-3 Days
- Packaging Details: 25kg Bag (Goni)
1030RG IOCL PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Types Of PP Granules | Natural |
Form | Granules |
Brand | IOCL |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | 1030RG |
Country of Origin | Made in India |
Melt Flow Index (2300C & 2.16 Kg) | 3.3 gm/10 min |
Density @ 23 deg C | 3 0.90 gm/cm |
Tensile Strength @ Yield (50 mm/min) | 35 MPa |
Elongation @ Yield (50 mm/min) | 12 % |
Flexural Modulus (1.3 mm/min) | 1550 MPa |
Notched Izod Impact Strength @ 23 deg C | 50 J/m |
Heat Deflection Temperature (0.46 N/m2) | 95 deg C |
Vicat Softening Point (10 N) | 156 deg C |
PP Homopolymer 1030RG is a natural colored grade produced by the latest Spheripol II Technology with following features:
- Exceptional processability
- Low water carry over
- Good balance of tenacity & elongation
Recommended Applications:
PP Homopolymer 1030RG is recommended for stretched tapes of Woven sacks like
- Fabrics for general packaging
- Cement & polymers packaging
- Food grains packaging
- Carpet packing
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT
R03RR HMEL PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Types Of PP Granules | Natural |
Form | Granules |
Brand | HMEL |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | R03RR |
Country of Origin | Made in India |
Melt Flow Index ( 230 deg C & 2.16 kg) | 3.4 g/10 min |
Tensile Strength @ Yield (50mm / min) | 34 MPa |
Tensile Elongation @ Yield (50mm / min) | 9 % |
Flexural Modulus | 1500 MPa |
Notch Izod Impact Strength ( 23 deg C) | 35 J/m |
Vicat Softening Point (10N) | 154 deg C |
Heat Deflection Temperature (0.455 MPa) | 95 deg C |
Polysure R03RR is Polypropylene Homopolymer, produced by Latest Novolen Technology & Primarily suitable for tape extrusion process applications. R03RR combines extremely low water carry-over with Exceptional processability, Good balance of tenacity & elongation for the production of tapes.
Recommended Applications:
- R03RR is recommended for Tape yarns, Monofilaments, Ropes, Leno bags, Strapping & Thermoforming application.
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT
HR003 MRPL PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Form | Granules |
Types Of PP Granules | Natural |
Brand | MRPL |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | HR003 |
Country of Origin | Made in India |
Melt Flow Index (I2.16 @230 deg C) | 3.5 g/10 min |
Tensile Strength at Yield | 34 MPa |
Tensile Elongation at Yield | 9 % |
Flexural Modulus | 1500 MPa |
Izod Impact Strength | 35 J /m |
Vicat Softening Point (10N) | 154 deg C |
Heat Deflection Temperature (0.455MPa) | 85 deg C |
Mangpol HR003 is a Polypropylene Homo polymer produced by latest solvent free gas phase polymerization using Novolen Technology. This polymer is primarily suitable for extrusion process. HR003 features excellent processability coupled with low water carryover and excellent balance between tenacity and toughness.
Recommended Applications:
- Stretched tapes for woven sacks for packaging Fertilizers, Cement, Polymer Pellets, Food Grains, Sugar, Carpet Backing.
- Leno Bags for Vegetable packaging, Stretched tapes for FIBC.
- Ropes and yarns.
- General purpose Thermoforming applications.
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT
HGX030SP Marlex PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Form | Granules |
Types Of PP Granules | Natural |
Brand | Marlex |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | HGX030SP |
Melt Flow Rate | 3 g/10 min |
Tensile Strength at Yield | 37 MPa |
Flexural Modulus, Secant | 1590 MPa |
Notched Izod Impact | 31 J/m |
Heat Deflection Temperature | 101 deg C |
- Woven industrial fabric and bag
- Rope and cordage
- Woven carpet backing
- Woven geotextile fabrics
- Large parts
- Good resistance to gas fading
This resin meets these specifications:
- FDA 21 CFR 177.1520(c)1.1. May be used in contact with all types of foods at conditions of use A through H per 21 CFR 176.170(c).
- All constituents of this resin are listed in Commission Regulation (EU) No 10/2011. Meets the requirements of Commission Regulation (EU) No 10/2011, Regulation (EC) No. 1935/2004, and Commission Regulation (EC) No 2023/2006.
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT
Moplen HP456J Lyondell Basell PP Raffia Granules
Minimum Order Quantity: 500 Kg
Product Brochure
Color | White |
Usage/Application | General Plastics |
Material | Poly Propylene |
Form | Granules |
Types Of PP Granules | Natural |
Brand | Lyondell Basell |
Packaging Type | Bag |
Packaging Size | 25KG |
Grade | Moplen HP456J |
Melt Flow Rate, (230 deg C/2.16 kg) | 3.4 g/10 min |
Flexural Modulus | 1500 N/mm2 |
Tensile Stress at Break, (23 deg C, 50 mm/min) | 21 N/mm2 |
Tensile Stress at Yield, (23 deg C, 50 mm/min) | 34 N/mm2 |
Tensile Strain at Break, (23 deg C, 50 mm/min) | 200 % |
Tensile Strain at Yield, (23 deg C, 50 mm/min) | 11 % |
Vicat Softening Temperature, (A50) | 156 deg C |
Deflection Temperature Under Load, (0.45 MPa, Unannealed) | 91 deg C |
Moplen HP456J Lyondell Basell PP Raffia Granules used for extrusion and thermoforming applications. Moplen HP456J is formulated with a low water-carry-over additive package. Typical applications are monofilaments, ropes and tapes.
Additional Information:
- Delivery Time: 2 - 3 DAYS
- Packaging Details: 25KG BAG (GONI) BAG SIZE 3 FT BY 1.5 FT